non-metallic inclusion
英 [ˈnəʊn məˈtælɪk ɪnˈkluːʒn]
美 [ˈnoʊn məˈtælɪk ɪnˈkluːʒn]
网络 非金属夹杂物; 非金属之介在物; 非金属夹杂
双语例句
- The wettability similarity was applied to the water model experiment, by which the mechanism of non-metallic inclusion agglomeration in liquid steel was studied.
通过夹杂物在中间包内去除的水模型实验，验证了润湿相似的重要性。 - The amount, size and distribution of non-metallic inclusion in different positions of hard wire steel with different diameters were investigated by optical microanalysis.
采用光学显微分析法在不同直径硬线钢的不同部位，分析了非金属夹杂物的数量、大小和分布特征。 - Distribution of non-metallic inclusion quantity in 304 stainless steel slab
304不锈钢连铸坯中的非金属夹杂物数量分布 - The results show that the fatigue fracture is caused by exceeded-quota sulphur and non-metallic inclusion enrichment in crack initiation, which induces stress concentrator in application.
表面裂纹源处存在夹杂物富集现象，在使用时引起应力集中，从而导致其疲劳断裂。 - Non-metallic inclusion control technology in medium and high carbon steel wire rod
中高碳钢线材中非金属夹杂物控制技术 - The removal of non-metallic inclusion during remelting occurred mainly in stages of formation of dropets on the consumable electrode tip and dropets falling through the slag.
电渣重熔过程中非金属夹杂物的去除主要发生在自耗电极端头熔滴形成期以及熔滴滴落穿过熔渣层阶段。 - Influence of Electromagnetic Brake in the Continuous Casting on the Non-metallic Inclusion of the Slab;
分析了高频磁场作用下熔体连续处理时夹杂物的去除效率。 - Fatigue and stress corrosion property tests were performed for a Cr-Ni-Mo-V-N steel, which had a non-metallic inclusion content exceeding standards.
对非金属夹杂物含量超标的CrNiMoVN材料进行了疲劳和应力腐蚀性能试验。 - The results show that the matrix composition of large-section prehardened-mould steel for plastic markedly influences the precipitation of non-metallic inclusion and the control of composition aided by Thermo-calc software package minimizes the amount of detrimental oxide inclusion.
结果表明，大截面预硬型塑料模具钢的基体成分显著影响非金属夹杂物的析出，并且利用Thermo-calc计算软件控制成分可以显著降低有害氧化物夹杂的含量。 - Effect of Non-metallic Inclusion on Property of Steel
非金属夹杂物对钢性能的影响 - Observations carried out by SEM showed that some defects existing on the wire surface and non-metallic inclusion was found on the fracture surface.
扫描电镜观察表明，微丝表面局部存在缺陷，而断口观察发现有非金属夹杂物存在； - Research on Ca and/ or Ba Alloy Deoxidation and Non-metallic Inclusion Controlling Technology
含钙钡合金脱氧和非金属夹杂物控制技术研究 - The possibility to produce zero non-metallic inclusion steel is analyzed and the metallurgical technology to produce zero non-metallic inclusion steel by using cold crucible levitation melting is discussed.
从理论上分析了零非金属夹杂钢制备的可能性。探讨了采用冷坩埚真空感应悬浮熔炼制备零夹杂钢的冶金工艺。 - Super Clean Steels and Zero Non-Metallic Inclusion Steels
超洁净钢和零非金属夹杂钢 - Coagulation Behavior of Micro-Sized Non-Metallic Inclusion in Molten Metal Processed by Ultrasound
超声波作用下金属液中微小夹杂物的凝聚过程 - The effect of the deformability, amount, size, shape and distribution of non-metallic inclusion, as well as spring surface defects, decarburization and surface treatment on fatigue property of high strength spring steel is reviewed in detail in this paper.
详尽地论述了非金属夹杂物的变形率、数量、尺寸、形状和分布以及表面缺陷、脱碳和表面处理对高强度弹簧钢疲劳性能的影响。 - The average value of impact absorbing energy at low temperature is low and the data are disperse under the action of hydrogen and non-metallic inclusion.
在氢和非金属夹杂物的共同影响下，低温冲击吸收功的平均数值较低，而且数据的离散度大； - Zero non-metallic inclusion steels are the steels in which inclusions are highly dispersed distribution and the inclusion dimension is ≤ 1 μ m.
零非金属夹杂钢为钢中夹杂物高度弥散、夹杂物尺寸≤1μm的钢。 - Effect of SiO_2 Non-Metallic Inclusion on Micro-Mechanical Behavior of Nickel-Base P/ M Superalloy
SiO2非金属夹杂物对镍基粉末高温合金微观力学行为的影响 - In order to increase the quality of castings, it has important meaning to study more effective methods to remove the non-metallic inclusion from molten magnesium alloy.
随着镁合金工业的快速发展，对其质量和性能的要求越来越高，因此研究出更多高效实用的去除非金属夹杂物方法，对提高镁合金铸件质量具有重要意义。 - Study of removal of non-metallic inclusion after liquid steel being heated CHEMI-CALLY in silicon alloys
用硅系发热剂化学加热后钢液中非金属夹杂物的研究 - The results indicate that multisource fatigue core appear in the axe surface non-metallic inclusion distributing place by bending and retortion circle stress;
结果表明辊轴在弯曲、扭转循环应力作用下，表面非金属夹杂物分布位置出现多源疲劳核心； - Study on the Non-Metallic Inclusion and Toughness of Steels
非金属夹杂物与钢的韧性研究 - It is suggested that the different effects of non-metallic inclusion on the fatigue fracture behaviors of the tested steels with different microstructures are the main reason for the above results.
对于铁素体+珠光体组织和均匀调质组织，非金属夹杂物对疲劳破坏行为的不同影响是上述实验料疲劳性能差异的主要原因。 - The effect of non-metallic inclusions on the mechanical properties is rather complicated, and lies on the location and size of the inclusion.
夹杂物对基体力学性能的影响是很复杂的，主要取决于其位置和尺寸。 - In modern external refining, the most important metallurgical reaction is carried out in ladle, including desulfuration, deoxidation, decarbonization, alloying, alloy composition trimming, degassing, removal of non-metallic inclusion, modification treatment and temperature control.
现代炉外精炼中最重要的冶金反应大多都是在钢包中进行的，包括脱硫、脱氧、脱碳、合金化、合金成分微调、脱气、去除非金属夹杂和变质处理及温度控制。